Comparative Study of the Antibacterial, Biodegradable, and Biocompatibility Properties of Composite and Bi-Layer Films of Chitosan/Gelatin Coated with Silver Particles.

The dressings are materials that can improve the wound-healing process in patients with medical issues. Polymeric films are frequently used as dressings with multiple biological properties. Chitosan and gelatin are the most used polymers in tissue regeneration processes. There are usually several configurations of films for dressings, among which the composite (mixture of two or more materials) and layered ones stand out (layers). This study analyzed the antibacterial, degradable, and biocompatible properties of chitosan and gelatin films in 2 configurations, composite and bilayer, composite. In addition, a silver coating was added to enhance the antibacterial properties of both configurations. After the study, it was found that the bilayer films have a higher antibacterial activity than the composite films, having inhibition halos between 23% and 78% in Gram-negative bacteria. In addition, the bilayer films increased the fibroblast cell proliferation process, reaching up to 192% cell viability after 48 h of incubation. On the other hand, composite films have greater stability since they are thicker, with 276 µm, 243.8 µm, and 239 µm compared to 236 µm, 233 µm, and 219 µm thick for bilayer films; and a low degradation rate compared to bilayer films.

The effect of Allium cepa extract on the chitosan/PLGA scaffolds bioactivity.

Allium cepa extracts (AC) allow the fabrication of a biomaterial that, together with chitosan and PLGA, could be osteoconductive and promote a better and faster regeneration of bone tissue, with biocompatibility and biomineralization properties. In this work, scaffolds were developed by the thermally induced phase separation (TIPS) technique. An in vitro bioactivity analysis was performed using simulated body fluid (SBF). Scanning electron microscopy (SEM), energy dispersion spectroscopy, and infrared spectroscopy were used for the scaffolds characterization. The results showed a structure with a pore size distribution between 50 and 100 µm, which allowed the uniform formation of biological apatite crystals on the surface of the scaffolds. The chitosan/policaprolactone/Allium cepa scaffold (ChPAC) showed the most promising results with a ratio of P/Ca between 1.6 and 1.7, a value very close to that of hydroxyapatite.